Immediately after the concrete or topping is laid, the surface is treated with LEVL Cure 100, a solution of acrylic resins in an organic solvent that forms a film for moisture-retaining curing. It is applied with a velour roller or sprayer; the film dries to degree 3 in no more than 2 hours. The coating is not decorative and gradually wears away: its purpose is to cure the hardening concrete, not to harden it. Packaging: 8 and 18 kg pails, 190 and 200 kg drums; shelf life 24 months.
| Manufacturer | LEVL (INGRI) — OOO “Ingri”, Saint Petersburg |
|---|---|
| Type | concrete impregnations and hardeners |
| Use | production workshops, warehouses and logistics, outdoor areas |
| Base | solution of acrylic resins in an organic solvent |
| Colour | clear liquid, colourless to yellowish; the coating is not decorative |
| Packaging | pails of 8 and 18 kg, drums of 190 and 200 kg |
| Application method | film-forming curing of freshly placed concrete and toppings; velour roller or sprayer |
| Application temperature | air and substrate +5…+30 °C; material +5…+25 °C; humidity up to 80 %; substrate 3 °C above the dew point |
| Curing | drying time to degree 3 no more than 2 h |
| Key properties | Density 0.90 ± 0.01 g/cm³; non-volatile content 16 ± 1 %; drying to degree 3 no more than 2 h |
| Consumption | 100–150 g/m² |
| Shelf life | 24 months; storage at −10…+25 °C |
| Standards | TU 2313-009-94613022-2006; GOST 28513, GOST 52487, GOST 19007 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Topping with quartz and corundum aggregate for workshops, warehouses and car parks under very significant loads; abrasion (wear) no more than 0.15 g/cm².
Three-component clear compound for the finishing layer of a 3D floor over decorative PVC film; Taber abrasion up to 50 mg.
Aqueous acrylic dispersion for priming concrete before LEVL Self and CemPol: reduces substrate water absorption and improves adhesion.
Thick-layer PU-cement coating for food and chemical production with impact and thermal loads, up to steam cleaning.
Water-based epoxy conductive layer over the copper circuit in LEVL antistatic floors; electrical resistance 10³–10⁵ ohm.
Smooth seamless epoxy coating for nuclear industry rooms subject to decontamination; Shore D hardness at least 70.