LEVL Coat 352 — wear-resistant polyurethane floor for car parks and warehouses
LEVL (INGRI)

LEVL Coat 352 — wear-resistant polyurethane floor for car parks and warehouses

Polyurethane floors

Car parks, car washes, cold warehouses and sales floors are among the sites LEVL Coat 352 is intended for. The two-component low-density polyurethane is laid in one layer over LEVL Coat 108 or 151 primer; it bridges cracks in concrete and becomes stronger with quartz sand. On open car parks the coating is protected with a UV-resistant varnish. Taber abrasion is up to 60 mg, elongation at break from 25 %, operating range from −40 to +80 °C; a fire safety certificate is available.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typepolyurethane floors
Usecar parks and ramps, outdoor areas, wet rooms, production workshops, retail and public buildings, warehouses and logistics, decorative, chemically resistant
Basepolyesters, fillers, pigments, special additives + aromatic polyisocyanate (two-component, low-density)
ColourRAL K-7 colour chart; uniform fine orange-peel texture
Packagingkit A+B = 22 kg (A: 20 l metal pail, B: 5 l jerrycan); A : B = 3.49 : 1 (by weight)
Application methodwear-resistant single-layer self-levelling coating that bridges cracks in concrete; with sand, of increased strength; over LEVL Coat 108 / 151 / Wetisol S-MP1 primer; pouring, squeegee or notched trowel, plastic spiked roller; optionally LEVL Coat 252 exp matt varnish; on open car parks, with a UV-resistant varnish
Application temperatureair +10…+30 °C (recommended +17…+23 °C); substrate +10…+30 °C (recommended +15…+25 °C); material +15…+25 °C; air humidity up to 80 %; substrate moisture no more than 5.0 % by weight (primer 108) or 4.0 % by weight (151, Wetisol S-MP1); 3 °C above the dew point
Curinglight foot traffic: +10 °C ~32 h, +20 °C ~24 h, +30 °C ~12 h; light loads ~6 / ~3 / ~2 days; full strength gain ~10 / ~7 / ~5 days; next coat after 12–48 h at +20 °C
Key propertiesTaber abrasion resistance (CS10/1000 g/1000 rev.) no more than 60 mg; Shore D hardness at least 55; relative elongation at break at least 25 %; tensile strength at break at least 10 MPa; adhesion at least 2.5 MPa (failure in the concrete); mix density 1.35 ± 0.05 kg/dm³; non-volatile content at least 99 %; pot life at least 30 min (+10 °C ~50 min, +20 °C ~30 min, +30 °C ~15 min); service temperature from minus 40 °C to +80 °C
Layer thicknessadmissible 1.5–3.0 mm; in highly filled systems 3.0–12.0 mm
Consumptiontheoretical 1.35 kg/m² at 1 mm thickness; 1.5 mm layer: 2.0 kg/m² (+ LEVL Coat 252 exp matt varnish 0.08 kg/m², optional); 3.0 mm system: main layer 1.95 kg/m² + quartz sand 0.1–0.3 mm 0.24 kg/m² and 0.3–0.9 mm 1.32 kg/m² + sealing 2 kg/m²
Shelf life6 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-007-94613022-06 (Amendment No. 1 in the test methods); fire safety V1, T1, D1, RP1: certificate of conformity No. RU C-RU.PB68.V.00715/21; coating requirements per SP 71.13330.2017 Table 8.12; test methods GOST 31992.1, GOST 31939, GOST 28574, GOST 24621, GOST 11262

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.