REKS® Epolit — three-component epoxy grout for anchor pockets and equipment
REKS

REKS® Epolit — three-component epoxy grout for anchor pockets and equipment

Epoxy grouts

Deep anchor pockets for large anchor bolts under heavy process equipment are filled with the three-component cold-curing epoxy grout REKS® Epolit. The highly filled material also serves as a high-strength grout for fixing critical equipment with dynamic loads — generators, turbines, compressors, diesel and gas engines, and pumps. After 3 days compressive strength is at least 80 MPa, after 7 days 100 MPa, flexural strength from 25 MPa; the pot life after mixing components A and B at +20 °C is at least 90 minutes.

Specifications

ManufacturerREKS — OOO “SPS”
Typeepoxy grouts
Useequipment foundations, anchoring of rebar and bolts, tunnels and metro, bridges and overpasses
Basethree-component highly filled cold-curing epoxy grout
Colourcomponent A — grey or red, component B — yellow, component C — mineral filler
Packagingkit 29.65 kg: component A 3.15 kg, component B 1.5 kg, component C 25 kg (metal pails)
Application methodREKS® EPOLIT — three-component high-strength highly filled cold-curing epoxy grout for filling deep anchor pockets when installing large anchor bolts; securing heavy process equipment to the foundation; as a high-strength grout for reliable fixing, in the design position, of critical equipment and installations subject to dynamic loads — generators, turbines, compressors; diesel and gas engines, pumps, electric…
Application temperaturecomponents conditioned for 48 h at +20 °C; substrate surface 3 °C above the dew point
Curingpot life after mixing A and B at +20 °C at least 90 min
Key propertiescompressive strength at 3 days: ≥80 MPa; compressive strength at 7 days: ≥100 MPa; flexural strength at 3 days: ≥25 MPa; modulus of elasticity at 3 days: ≥5,000 MPa; adhesion to metal at 3 days: ≥6 MPa; adhesion to concrete at 3 days: exceed the cohesion of concrete; gel time at 20 °C: ≥90 min; density of the mixed compound: ≥2.1 g/cm³; water absorption at 1 day: ≤0.4 %; coefficient of linear thermal expansion, 1/K: 30·10⁻⁶
Shelf life12 months from the date of manufacture

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.