LEVL Coat 307 — low-density epoxy self-levelling floor
LEVL (INGRI)

LEVL Coat 307 — low-density epoxy self-levelling floor

Epoxy floors

LEVL Coat 307 is a lightweight counterpart of LEVL Coat 303: thanks to its lower density, the compound takes more quartz sand in the mix, up to +67 %. It is used to make self-levelling and highly filled, smooth and textured coatings over the range’s epoxy primers. Shore D hardness is at least 70, compressive and flexural strength at least 60 MPa, Taber abrasion up to 55 mg. It is used in retail, healthcare, warehouses and workshops, car parks, pharmaceutical and chemical production and rooms with a “wet cycle”.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Useretail and public buildings, food and pharmaceutical, chemically resistant, warehouses and logistics, production workshops, car parks and ramps, wet rooms
Baseepoxy resin (two-component low-density compound)
ColourRAL colours; uniform gloss finish
Packagingkits of 2.46; 10 and 25 kg; A : B = 3.17 : 1.00 (by weight)
Application methodself-levelling and highly filled, smooth and textured floor coatings over LEVL Coat 101 / 102 W / 103 / 104 Rapid / 108 / 118 primer: pouring, squeegee or notched trowel, rolling with a spiked roller; filling with quartz sand 1.5 : 1.0 (+67 %); textured: broadcast to excess with 0.3–0.9 mm sand and a finishing coat
Application temperatureair and substrate +10…+30 °C (recommended +17…+23 °C); material +15…+25 °C; air humidity no more than 80 %; substrate moisture no more than 5 % (primers 101/103/104 Rapid/108/118) or no more than 10 % (102 W); 3 °C above the dew point
Curinglight loads / recoat interval: +10 °C ~32 h, +23 °C ~16 h, +30 °C ~12 h; foot traffic: ~6 / ~3 / ~2 days; full strength gain: ~10 / ~7 / ~5 days; next coat no earlier than 16 h and no later than 48 h at 23 °C
Key propertiesShore D hardness (7 days) at least 70; ultimate compressive strength (7 days) at least 60 MPa; flexural at least 60 MPa; tensile strength at break at least 10 MPa; adhesion to concrete at least 2.5 MPa (failure in the concrete); Taber abrasion (CS10 / 1000 g / 1000 rev.) no more than 55 mg; density 1.35 ± 0.05 g/cm³; non-volatile content at least 96 %; pot life +10 °C ~60 min, +20 °C ~30 min, +30 °C ~15 min; service temperature from −10 to +60 °C (highly filled: short-term up to +90 °C); chemical resistance: on request
Layer thicknessself-levelling unfilled 1–3 mm; self-levelling filled (+67 % sand) 1.5–5.0 mm; highly filled 3–12 mm
Consumptionsmooth filled 2 mm: 2.01 kg/m² + quartz sand 0.1–0.3 mm 1.34 kg/m²; textured highly filled 6 mm: 2.34 kg/m² + filler sand 0.1–0.3 mm 1.08 kg/m² + broadcast 0.3–0.9 mm 7.38 kg/m² + finishing coat 0.75 kg/m²; theoretically per 1 mm: unfilled 1.35 kg/m², filled (1.5 : 1.0) 1.67 kg/m²
Shelf life12 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-006-94613022-2006; works per SP 29.13330.2011 and SP 71.13330.2017; test methods GOST 31992.1, GOST R 31939, GOST 24621, GOST 11262, GOST 28574

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.

Other materials by LEVL (INGRI)